Film Faced Plywood

Features:

1) Made of climate-resistant one grade Dynea WBP glue
2) Film: imported from Finland and Dynea, weight 185g/m2
3) Anti-abrasive, winkles-resistant and anti-erosive
4) If put in boiling water for 48 hours, it is still glue-sticking and non-deformed
5) If used abide by the illustrations strictly, it can be reused more than 50 times, thus reducing the cost greatly
and avoiding the disadvantages: rustily and erosive of iron mould
6) Solves the problems of leaking and rough surface during constructing process
7) Particularly suitable for watering concrete project because it can make the concrete surface smooth and flat
8) Can decorate or brush directly without any renovation
9) Realizing a higher economic profits
10) Physical mood is better than iron moulds and can satisfy the requirements of constructing mould, while
the iron ones are easy to be deformed and can hardly recover its smoothness even after repairing

Application:

Suitable for construction, concrete formwork (The panels hold the concrete in a mould until it sets), and widespread on beams, bridges, large deck forms, dam , and other civil engineering projects.

Parameters:

Product Name	FINLAND DYNEA FILM FACED PLYWOOD
Size	1220x2440mm, 1200x2400, 1250x2500mm or customized
Thickness	12~25mm
Thickness Tolerance	+/-0.5mm
Face/Back	Imported Finland dynea brown film or anti-slip film (black or brown)
Core	Poplar, Combi, Eucalyptus (Hardwood), Birch, etc.
Edge Treatment	Sealed by waterproof paint or transparent wbp glue
Glue	WBP Phenolic Glue
Corrosion Resistance	No pollution to concrete surface
Resistance	Good weather resistance, can with stand temperature -10℃-50℃
Technology:	Two times hot pressed, three times hot pressed or more
Loading quantity:	1x20GP, 8pallets, 25CBM; 1X40HQ, 18pallets, 55CBM
Payment terms:	(1)TT30% deposit in advance , the balance be paid before shipping (2)100% LC at sight
Delivery time:	15-25working days after confirm deposit
Package:	Standard export MDF boards packing with belt.
Technical Parameters	Moisture Content	6%~12%
	Dip-peeling performance	0
	Water Absorption	≤10%
	Modulus of Elasticity	Longitudinal≥5000Mpa
	Modulus of Elasticity	Transverse≥4000MPa
	Static Bending Strength	≥30Mpa
	Surface Bonding Strength	≥1.60Mpa
	Internal Bonding Strength	≥0.90Mpa
	Screw Holding Ability	Face	≥2000N
		Edge	≥1600N

PROJECTS